Grade |
Structure |
Block Ratio S/I |
SI Content % |
Tensile Strength Mpa |
Hardness |
MFR (g/10min, 200ºC, 5kg) |
Toluene Solution Viscosity at 25ºC and 25%, mpa.s |
|
1105 |
Linear |
15/85 |
0 |
13 |
41 |
10 |
1250 |
|
1106 |
Linear |
16/84 |
16.5 |
12 |
40 |
11 |
900 |
|
1209 |
Linear |
29/71 |
0 |
15 |
61 |
10 |
320 |
|
1124 |
Linear |
14/86 |
25 |
10 |
38 |
10 |
1200 |
|
1126 |
Linear |
16/84 |
50 |
5 |
38 |
11 |
900 |
|
4019 |
Star-shaped |
19/81 |
30 |
10 |
45 |
12 |
350 |
|
1125 |
Linear |
25/75 |
25 |
10 |
54 |
12 |
300 |
|
1128 |
Linear |
15/85 |
38 |
12 |
33 |
22 |
600 |
|
1125H |
Linear |
30/70 |
25 |
13 |
58 |
10-15 |
200-300 |
|
1108 |
Coupling linear |
16/84 |
20 |
10 |
40 |
15 |
850 |
|
4016 |
Star-shaped |
18/82 |
75 |
3 |
44 |
23 |
500 |
|
2036 |
Mixed |
15/85 |
15 |
10 |
35 |
10 |
1500 |
合成橡胶 SIS